ALUMINUM
Composition in percents: maximum unless shown as a range
| Alloy |
Silicon
| Iron
| Copper
| Manganese
| Magnesium
| Chromium
| Vanadium
| Nickel
| Zinc
| Titanium
| Each
| Total
| Aluminum
Min.
|
| 1100 |
0.95 Si + Fe
| 0.05-0.20
| 0.05
| ....
| ....
| ....
| ....
| 0.10
| ....
| 0.05
| 0.15
| 99.00
|
| 2011 |
0.04
| 0.7
| 5.0-6.0
| ....
| ....
| ....
| ....
| ....
| 0.30
| ....
| 0.05
| 0.15
| Remainder
|
| 2014 |
0.50 -1.2
| 0.7
| 3.9-5.0
| 0.40-1.2
| 0.20-0.8
| 0.10
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 2017 |
0.20 - 0.8
| 0.7
| 3.5-4.5
| 0.40-1.0
| 0.40-0.8
| 0.10
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 2024 |
0.50
| 0.50
| 3.8-4.9
| 0.30-0.9
| 1.2-1.8
| 0.10
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 2036 |
0.50
| 0.50
| 2.2-3.0
| 0.10-0.40
| 0.30-0.6
| 0.10
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 2124 |
0.20
| 0.30
| 3.8-4.9
| 0.30-0.9
| 1.2-1.8
| 0.10
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 2219 |
0.20
| 0.30
| 5.8-6.8
| 0.20-0.40
| 0.02
| ....
| 0.05-0.15
| ....
| 0.10
| 0.02-0.10
| 0.05
| 0.15
| Remainder
|
| 2618 |
0.10-0.25
| 0.9-1.3
| 1.9-2.7
| ....
| 1.3-1.8
| ....
| ....
| 0.9-1.2
| 0.10
| 0.04-0.10
| 0.05
| 0.15
| Remainder
|
| 3003 |
0.6
| 0.7
| 0.05-0.20
| 1.0-1.5
| ....
| ....
| ....
| ....
| 0.10
| ....
| 0.05
| 0.15
| Remainder
|
| 3105 |
0.6
| 0.7
| 0.30
| 0.30-0.8
| 0.20-0.8
| 0.20
| ....
| ....
| 0.40
| 0.10
| 0.05
| 0.15
| Remainder
|
| 5005 |
0.30
| 0.7
| 0.20
| 0.20
| 0.50-1.1
| 0.10
| ....
| ....
| 0.25
| ....
| 0.05
| 0.15
| Remainder
|
| 5052 |
0.25
| 0.40
| 0.10
| 0.10
| 2.2-2.8
| 0.15-0.35
| ....
| ....
| 0.10
| ....
| 0.05
| 0.15
| Remainder
|
| 5083 |
0.40
| 0.40
| 0.10
| 0.40-1.0
| 4.0-4.9
| 0.05-0.25
| .....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 5086 |
0.40
| 0.50
| 0.10
| 0.20-0.7
| 3.5-4.5
| 0.05-0.25
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 5454 |
0.25
| 0.40
| 0.10
| 0.50-1.0
| 2.4-3.0
| 0.05-0.20
| ....
| ....
| 0.25
| 0.20
| 0.05
| 0.15
| Remainder
|
| 5456 |
0.25
| 0.40
| 0.10
| 0.50-1.0
| 4.7-5.5
| 0.05-0.20
| ....
| ....
| 0.25
| 0.20
| 0.05
| 0.15
| Remainder
|
| 6061 |
0.40-0.8
| 0.7
| 0.15-0.40
| 0.15
| 0.8-1.2
| 0.04-0.35
| ....
| ....
| 0.25
| 0.15
| 0.05
| 0.15
| Remainder
|
| 6063 |
0.20-0.6
| 0.35
| 0.10
| 0.10
| 0.45-0.9
| 0.10
| ....
| ....
| 0.10
| 0.10
| 0.05
| 0.15
| Remainder
|
| 7050 |
0.12
| 0.15
| 2.0-2.6
| 0.10
| 1.9-2.6
| 0.04
| ....
| ....
| 5.7-6.7
| 0.06
| 0.05
| 0.15
| Remainder
|
| 7075 |
0.40
| 0.50
| 1.2-2.0
| 0.30
| 2.1-2.9
| 0.18-0.28
| ....
| ....
| 5.1-6.1
| 0.20
| 0.05
| 0.15
| Remainder
|
| 7150 |
0.12
| 0.15
| 1.9-2.5
| 0.10
| 2.0-2.7
| 0.04
| ....
| ....
| 5.9-6.9
| 0.06
| 0.05
| 0.15
| Remainder
|
| 7178 |
0.40
| 0.50
| 1.6-2.4
| 0.30
| 2.4-3.1
| 0.18-0.28
| ....
| ....
| 6.3-7.3
| 0.20
| 0.05
| 0.15
| Remainder
|
| 7475 |
0.10
| 0.12
| 1.2-1.9
| 0.06
| 1.9-2.6
| 0.18-0.25
| ....
| ....
| 5.2-6.2
| 0.06
| 0.05
| 0.15
| Remainder
|
The above alloys can be supplied in all tempers, shapes and sizes